Raw materials
CA Series-550CA30 PEEK Carbon Fiber Reinforcement |
||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
|
Material Properties |
Test Method |
Conditions |
Units |
770G |
|
Mechanical Data |
||||
|
Tensile Strength |
ISO 527 |
B reak,23℃ |
MPa |
- |
|
Y ield,23℃ |
MPa |
100 |
||
|
Tensile Elogation |
ISO 527 |
Break,23℃ |
% |
45 |
|
Flexural Strength |
ISO 178 |
Break,23℃ |
MPa |
- |
|
Y ield,23℃ |
MPa |
165 |
||
|
Fleoural Modulus |
ISO 178 |
23℃ |
Gpa |
4.1 |
|
Compressive Strength |
ISO 604 |
23℃ |
MPa |
125 |
|
Charpy Impact Strength |
ISO 179/leA |
Notched |
kJm-2 |
7 |
|
ISO 179/IU |
Unnotched |
kJm-2 |
- |
|
|
Izod Impact Strength |
ISO 180/A |
Notched |
kJm-2 |
7.5 |
|
ISO 180/U |
Unnotched |
kJm-2 |
- |
|
|
Mould Shrinkage |
ISO 294-4 |
Along flow |
% |
1 |
|
Across flow |
% |
1.3 |
||
|
Thermal Data |
||||
|
Melting Point |
ISO 11357 |
|
℃ |
343 |
|
Glass Tansition (Tg) |
ISO 11357 |
Onset |
℃ |
143 |
|
Special Heat Capacity |
DSC |
23℃ |
kj kg-1℃-1 |
2.2 |
|
Coefficient of Thermal Expansion |
ISO 11359 |
Along flow below Tg |
ppm K-1 |
45 |
|
Along flow above Tg |
ppm K-1 |
120 |
||
|
Heat Deflecion Temperature |
ISO 75A-f |
1.8Mpa |
℃ |
152 |
|
Thermal Conductivity |
ASTM C177 |
23℃ |
W m-1K-1 |
0.29 |
|
Flow |
||||
|
MeltIndex |
ISO 1133 |
380℃,5kg |
g10min-1 |
10 |
|
Miscellaneous |
||||
|
Density |
ISO 1186 |
Crystalline |
gcm-3 |
1.3 |
|
Amorphous |
gcm-3 |
1.26 |
||
|
Shore D Hardness |
ISO 868 |
23℃ |
|
85 |
|
Water Absorption(3.2mm thick Tensile Bar) |
ISO 62-1 |
24h,23℃ |
% |
0.07 |
|
by immersion |
|
Equilib riu m,23℃ |
% |
0.4 |
|
Electrical Data |
||||
|
Dielectric Strength |
IEC 60243-1 |
2mm |
kV mm-1 |
23 |
|
Comparative Tracking Index |
IEC 60112 |
|
V |
150 |
|
Dielectric Constant |
IEC 60250 |
23℃,1kHz |
|
3.1 |
|
23℃,50kHz |
|
3 |
||
|
Loss Tangent |
IEC 60250 |
23℃,1MHz |
|
0.004 |
|
Volume Resistivity |
IEC 60093 |
23℃,1V |
Ω cm |
10 16 |
|
275℃ |
Ω cm |
10 9 |
||
As a peek material supplier, we will do our best to meet all the needs of customers.
Good deal: buying from seller
|
This page is about importers and exporters of CA Series-550CA30 PEEK Carbon Fiber Reinforcement Search in a category : Raw materials Search in a category : series, carbon, peek, fiber, reinforcement, 550ca30 |
Monday, September 07, 2015
- Feature (click here for details) - - Under the LAN can support more than 10 simultaneous client connections cameras, image lag within 100 milliseconds, supports standard streaming media network protocols, network 8 M per channel bit rate case, no mosaic - The DSP processor...
Tuesday, August 11, 2015
Price : 1$ ~30 $
One Lus International is a professional gear shift lock manufacturer in Taiwan and provides a series of gear shift lock to meet customer's needs. The side opening gear shift lock is easy to operate and convenient to use. The top opening gear shift lock is suitable for automatic & manual...
Tuesday, December 23, 2025
Quantity : Customers - Price : Negotiable
Aerona Beauty carry a wide selection of Thinning Shears made from top quality Stainless steel AISI-440C & AISI-420. Each pair of Thinning Shears cuts with consistency and with a comfortably smooth action. These Scissors are Mirror Polished,Sand Finished and Satin Finished.Hair...