ASTM A213 T11 Seamless alloy pipe |
UNS Designation | K11597 |
Carbon | 0.05-0.15 |
Manganese | 0.30–0.60 |
Phosphorus | 0.025 |
Sulfur | 0.025 |
Silicon | 0.50-1.00 |
Nickel | … |
Chromium | 1.00-1.50 |
Molybdenum | 0.44-0.65 |
Vanadium | … |
Boron | … |
Niobium | … |
Nitrogen | … |
Aluminum | … |
Tungsten | … |
Other Elements | … |
Tensile strength(min) | 415Mpa |
Yield strength(min) | 220Mpa |
Elongation | 30% |
Delivery condition | annealed |
1.1 This specification covers seamless ferritic and austenitic steel boiler, superheater, and heat-exchanger tubes, designated Grades T91, TP304, etc. These steels are listed in Tables 1 and 2.
1.2 Grades containing the letter, H, in their designation, have requirements different from those of similar grades not containing the letter, H. These different requirements provide higher creep-rupture strength than normally achievable in similar grades without these different requirements.
1.3 The tubing sizes and thicknesses usually furnished to this specification are 1/8 in. [3.2 mm] in inside diameter to 5 in. [127 mm] in outside diameter and 0.015 to 0.500 in. [0.4 to 12.7 mm], inclusive, in minimum wall thickness or, if specified in the order, average wall thickness. Tubing having other diameters may be furnished, provided such tubes comply with all other requirements of this specification.
1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard. The inch-pound units shall apply unless the “M” designation of this specification is specified in the order.
TABLE 1 Chemical Composition Limits, %A, for Low Alloy SteelA Maximum, unless range or minimum is indicated. Where ellipses (…) appear in this table, there is no requirement, and analysis for the element need not be determined or reported.
B It is permissible to order T2 and T12 with a sulfur content of 0.045 max. See 16.3.
C Alternatively, in lieu of this ratio minimum, the material shall have a minimum hardness of 275 HV in the hardened condition, defined as after austenitizing and cooling to room temperature but prior to tempering. Hardness testing shall be performed at mid-thickness of the product. Hardness test frequency shall be two samples of product per heat treatment lot and the hardness testing results shall be reported on the material test report.
Referenced Documents (purchase separately)
Good deal: buying from seller
This page is about importers and exporters of ASTM A213 T11 Seamless alloy pipe Search in a category : Raw materials Search in a category : seamless, pipe, a213, astm, alloy |
Wednesday, September 07, 2022
漫画亚克力钥匙扣单面印刷 我们是一家专业的亚克力钥匙扣制造商。我们在这个领域有超过 12 年的经验,我们有自己的工厂。我们可以根据您的要求制作任何不同款式的亚克力钥匙扣。 我们可以以质量和合理的价格制作漫画亚克力钥匙扣,我们相信您会对我们的产品感到满意 。 我们的亚克力钥匙扣是送给贵公司的很好的促销礼物,它有很多优点: 1.携带方便。我们有不同尺寸的漫画亚克力钥匙扣,因此您可以选择适合您需求的一款。 2.It is inexpensive and light in weight, which makes it easy to carry around with...
Friday, November 25, 2016
Quantity : SHS Cerami - Price : 1 000,00 €
SHS- self -igniting alumina ceramic composite pipe is the national " 863 " program in the field of new materials , and the successful implementation of the industrialization of high-tech achievements. The products are of corundum (a-AL2O3) ceramic intermediate layer , three layers...
Friday, November 18, 2022
These days, more and more homeowners are ditching traditional white or brown wood cabinetry in favor of rich grays in their kitchen. And it's not a surprising trend because unlike some color schemes, grey bedroom doors offer the perfect balance of warmth and neutrality, working well...