Everything else / Bulk
Carbon Black |
Standard |
N110 |
N115 |
N121 |
N134 |
N219 |
N220 |
|
||||||
Item |
||||||
Ioding AdsorptionNumber g/kg |
145±8 |
160±8 |
121±7 |
142±8 |
118±7 |
121±7 |
DBP Absorption Number 10-5M3/kg |
113±7 |
113±7 |
132±8 |
127±7 |
78±7 |
114±7 |
DBP Compressed Sample10-5M3/kg |
89-105 |
89-105 |
103-119 |
95-111 |
67-91 |
90-106 |
CTAB surface Area103M2/kg |
117-135 |
119-137 |
112-130 |
124-144 |
98-116 |
102-120 |
Nitrogen Surface Area103M2/kg |
120-134 |
129-145 |
115-129 |
135-151 |
109-123 |
112-126 |
Tint Strength % |
115-131 |
115-131 |
111-127 |
123-139 |
115-131 |
108-124 |
Heating Loss %≤ |
3 |
3 |
3 |
3 |
2.5 |
2.5 |
Ash Content % |
0.7 |
0.7 |
0.7 |
0.7 |
0.7 |
0.7 |
45μm Sieve Residue % ≤ |
0.1 |
0.1 |
0.1 |
0.1 |
0.1 |
0.1 |
500μm Sieve Residue % ≤ |
0.001 |
0.001 |
0.001 |
0.001 |
0.001 |
0.001 |
Impurity |
no |
no |
no |
no |
no |
no |
stress at 300% Elongation Mpa |
-3.5±1.6 |
-3.4±1.6 |
-0.4±1.6 |
-1.8±1.6 |
-3.9±1.6 |
-2.3±1.6 |
Characteristics of vulcanized rubber |
N110: High reinforcing, super abrasion |
|||||
N115: High reinforcing, super abrasion |
||||||
N121: High reinforcing, super abrasion, high modulus |
||||||
N134: High reinforcing |
||||||
N219: High reinforcing, low modulus, good elongation and resistance to tearing, good flex resistance |
||||||
N220: High reinforcing, high tear resistance, good processing |
||||||
Standard |
N375 |
N539 |
N550 |
N660 |
N762 |
N774 |
|
||||||
Item |
||||||
Iodine Adsorption Number g/kg |
90±7 |
43±6 |
43±6 |
36±6 |
27±6 |
29±6 |
DBP Absorption Number 10-5M3/kg |
114±7 |
111±7 |
121±7 |
90±7 |
65±6 |
72±7 |
DBP Compressed Sample10-5M3/kg |
88-104 |
73-89 |
77-93 |
66-82 |
53-65 |
57-69 |
CTAB surface Area103M2/kg |
87-105 |
34-48 |
35-49 |
29-43 |
23-35 |
23-35 |
Nitrogen Surface Area103M2/kg |
86-100 |
33-45 |
34-46 |
29-41 |
24-34 |
25-35 |
Tint Strength % |
106-122 |
- |
- |
- |
- |
- |
Heating Loss %≤ |
2.5 |
1.5 |
1.5 |
1.5 |
1.5 |
1.5 |
Ash Content % |
0.7 |
0.7 |
0.7 |
0.7 |
0.7 |
0.7 |
45μm Sieve Residue % ≤ |
0.1 |
0.1 |
0.1 |
0.1 |
0.1 |
0.1 |
500μm Sieve Residue % ≤ |
0.001 |
0.001 |
0.001 |
0.001 |
0.001 |
0.001 |
Impurity |
no |
no |
no |
no |
no |
no |
stress at 300% Elongation Mpa |
0.1±1.6 |
-1.6±1.6 |
-0.9±1.6 |
-2.6±1.6 |
-4.9±1.6 |
-4.1±1.6 |
Characteristics of vulcanized rubber |
N375: medium-high reinforcing, high modules and hardness, smooth surface of extrusion |
|||||
N539: Medium-high reinforcing, high modulus and hardness, smooth surface of extrusion |
||||||
N550: Medium-high reinforcing, high modulus and hardness, smooth surface of extrusion |
||||||
N660: medium-high reinforcing and modulus, good flex resistance, low heat buildup |
||||||
N762: low reinforcing |
||||||
N774: semi-reinforcing, good elongation, high resilience, low compressed deformation |
||||||
Standard |
N234 |
N326 |
N330 |
N339 |
N347 |
N351 |
|
||||||
|
||||||
|
||||||
Item |
||||||
Coding Adsorption Number g/kg |
120±7 |
82±7 |
82±7 |
90±7 |
90±7 |
68±7 |
DBP Absorption Number 10-5M3/kg |
125±7 |
72±7 |
102±7 |
120±7 |
124±7 |
120±7 |
DBP Compressed Sample10-5M3/kg |
94-110 |
62-74 |
80-96 |
91-107 |
91-107 |
87-103 |
CTAB surface Area103M2/kg |
110-128 |
74-92 |
73-91 |
84-102 |
78-96 |
64-82 |
Nitrogen Surface Area103M2/kg |
112-126 |
71-85 |
71-85 |
84-98 |
78-92 |
64-78 |
Tint Strength % |
115-131 |
103-119 |
96-112 |
103-119 |
97-113 |
92-108 |
Heating Loss %≤ |
2.5 |
2.5 |
2.5 |
2.5 |
2.5 |
2.5 |
Ash Content % |
0.7 |
0.7 |
0.7 |
0.7 |
0.7 |
0.7 |
45μm Sieve Residue % ≤ |
0.1 |
0.1 |
0.1 |
0.1 |
0.1 |
0.1 |
500μm Sieve Residue % ≤ |
0.001 |
0.001 |
0.001 |
0.001 |
0.001 |
0.001 |
Impurity |
no |
no |
no |
no |
no |
no |
stress at 300% Elongation Mpa |
-0.4±1.6 |
-3.9±1.6 |
-0.9±1.6 |
0.6±1.6 |
0.2±1.6 |
0.8±1.6 |
Characteristics of vulcanized rubber |
N234: High reinforcing, high abrasion, high modulus, good dispersion |
|||||
N326: Medium-high reinforcing, low modules, good elongation and resistance to tearing, good flex resistance |
||||||
N330: medium-high reinforcing and modulus, good processing |
||||||
N339: medium-high reinforcing, high modulus and hardness, good processing |
||||||
N347: medium-high reinforcing, high modulus and hardness, good processing |
||||||
N351: medium-high reinforcing, high modulus and hardness, good processing |
Packing of Carbon Black
20kg/package: 1MT/Pallet
1000kg/package: 1MT/Pallet
Or customized
Application of Carbon Black
Carbon black is mainly used as reinforcing filler in tyres and other rubber products during the vulcanization process to improve the tensile strength and wear resistance of styrene-butadiene, such as rubber conveyor belts, rubber hose, Airsprings and other rubber chemicals.
As one of carbon black suppliers, we can provide high quality carbon black N220, carbon black N330, carbon black N660 for sale, if you have needs, please contact us.
If you are looking for a reliable rubber raw material manufacturer, please choose us, and we will be your best partner.
Good deal: buying from seller
This page is about importers and exporters of Carbon Black Search in a category : Everything else / Bulk Search in a category : black, carbon |
Tuesday, May 19, 2009
we supply high quality ladies nightgowns,morninggowns,pyjamas and t-shirts according to customer's specifications and label. combed quality %100 cotton,single jersey,30/1 short or long sleeve tubular printed one or two piece packed in seperate polybag sizes:36/38-52/54Location : kusdili...
Thursday, January 15, 2009
Desiccated Coconut Desiccated coconut high fat fine and mediumg grades: - Moisture: 3% max, - FFA: 0.3 % max, - Oil content: 62% min, - Free from ecoli or bactereia, no foreign matterLocation : 20/5 Dinh Bo Linh str Binh Thanh Distr, 84 Ho Chi Minh, Contact : Smith Nguyen, 84(08)35114928
Saturday, July 12, 2014
Quantity : 5000 - Price : 1,50 euros
Bonjour, Vends maillots de bain licence High School Musical. Taille: 128-134-140-146-152-158-164-170. Prix. 1,50 euros par 500 pièces. Mail. nekortex@gmail.com Mobile. 06.52.83.92.08 Mr Ben. Location : 18 rue d'albert, 95140 Garges les gonesses, Contact : Ben Mr, 06 52 83 92...