ASTM A213 T91 Seamless alloy tube |
UNS Designation | K31545 |
Carbon | 0.05–0.15 |
Manganese | 0.30–0.60 |
Phosphorus | 0.025 |
Sulfur | 0.025 |
Silicon | 0.50–1.00 |
Nickel | … |
Chromium | 2.65–3.35 |
Molybdenum | 0.80–1.06 |
Vanadium | … |
Boron | … |
Niobium | … |
Nitrogen | … |
Aluminum | … |
Tungsten | … |
Other Elements | … |
Tensile strength(min) | 415Mpa |
Yield strength(min) | 220Mpa |
Elongation | 30% |
Delivery condition | annealed |
1.1 This specification covers seamless ferritic and austenitic steel boiler, superheater, and heat-exchanger tubes, designated Grades T91, TP304, etc. These steels are listed in Tables 1 and 2.
1.2 Grades containing the letter, H, in their designation, have requirements different from those of similar grades not containing the letter, H. These different requirements provide higher creep-rupture strength than normally achievable in similar grades without these different requirements.
1.3 The tubing sizes and thicknesses usually furnished to this specification are 1/8 in. [3.2 mm] in inside diameter to 5 in. [127 mm] in outside diameter and 0.015 to 0.500 in. [0.4 to 12.7 mm], inclusive, in minimum wall thickness or, if specified in the order, average wall thickness. Tubing having other diameters may be furnished, provided such tubes comply with all other requirements of this specification.
1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard. The inch-pound units shall apply unless the “M” designation of this specification is specified in the order.
TABLE 1 Chemical Composition Limits, %A, for Low Alloy SteelA Maximum, unless range or minimum is indicated. Where ellipses (…) appear in this table, there is no requirement, and analysis for the element need not be determined or reported.
B It is permissible to order T2 and T12 with a sulfur content of 0.045 max. See 16.3.
C Alternatively, in lieu of this ratio minimum, the material shall have a minimum hardness of 275 HV in the hardened condition, defined as after austenitizing and cooling to room temperature but prior to tempering. Hardness testing shall be performed at mid-thickness of the product. Hardness test frequency shall be two samples of product per heat treatment lot and the hardness testing results shall be reported on the material test report.
Referenced Documents (purchase separately)
Good deal: buying from seller
This page is about importers and exporters of ASTM A213 T91 Seamless alloy tube Search in a category : Second hand goods Search in a category : astm, alloy, tube, seamless, a213 |
Saturday, July 09, 2022
Quantity : 30000TONS - Price : 1-20USD/KG
GRAPHITE PLATE FOR SALE With the development of modern science and technology and industry, carbon china graphite plate has become an indispensable industrial product, and its application is more and more extensive. Graphite plate is a material with electrical conductivity, high temperature...
Wednesday, November 25, 2020
Quantity : 5000 - Price : 8,00 €
SHINING JINS ENTERPRISE specializing in manufacturing & designing cold forge Top Plate (Washer) and Pole piece (T-Yoke) for Loud-Speaker and alarms raw driver in Taiwan. We offer a complete range of Top Plate (Washer) and Pole piece (T-Yoke) uses in Home speaker, P.A. Speaker...
Wednesday, November 25, 2020
Quantity : 5000 - Price : 8,00 €
SHINING JINS ENTERPRISE specializing in manufacturing & designing cold forge Top Plate (Washer) and Pole piece (T-Yoke) for Loud-Speaker and alarms raw driver in Taiwan. We offer a complete range of Top Plate (Washer) and Pole piece (T-Yoke) uses in Home speaker, P.A. Speaker...