Calcined Bauxite

Calcined Bauxite Introduction

Calcined Bauxite is obtained by firing (heating) the superior grade Bauxite at high temperature (from 850 degree to 1600 degree). This removes moisture thereby increasing the alumina content. Compared to an alumina content of about 57 % to 58 % in raw Bauxite, rotary kiln calcined bauxite has an alumina content of 75 % to 90 %. The heating is carried out in rotary kilns. Calcination is done at different temperatures ranging from 850 degree to 1600 degree depending upon the customer's application.

Calcined Bauxite Introduction

Calcined Bauxite is obtained by firing (heating) the superior grade Bauxite at high temperature (from 850 degree to 1600 degree). This removes moisture thereby increasing the alumina content. Compared to an alumina content of about 57 % to 58 % in raw Bauxite, Calcined Bauxite has an alumina content of 75 % to 90 %. The heating is carried out in rotary kilns. Calcination is done at different temperatures ranging from 850 degree to 1600 degree depending upon the customer's application.

Oreworld trade (Tangshan) co., Ltd. calcined bauxite manufacturers has been engaged in exporting business for about 20 years. We are dealing in fields of special cements, refractory materials and ore products.

For the special cement products, it includes calcium aluminate cements (CA cement) and calcium sulfoaluminate cements (CSA cement/CSA binder). The CSA cement is more and more imported by GRC manufacturers and dry mix mortars manufactures because of its higher performance compare to the Portland cement such as fast setting time, rapid hardening and high strength in 3 days. It is also widely used in bridge building the highway building and cold weather concreting.